 If you are looking for a quality PVC foam trimboard which features the latest in product technology and which comes with the kind of personal service you need, call AmeriLux International, LLC. Our Coverbord™ PVC foam trimboards are an effective alternative to traditional wood trims and are ideal for trim, fascia or detailed moldings.
UNIFORMITY
- Solid Profile with No Voids
- Consistent Thickness
- Square Edges on All Four Sides
- Premium Lengths
- Cell Structure Perfect for Milling
|
DURABILITY
- Impervious to Insects and Moisture
- Will Not Rot, Cup, Split, Twist or Warp
- Doesn't Require Paint for Protection
- Excellent for Ground & Masonry Contact
|
WORKABILITY
- Same Tools and Fasteners as Wood
- Can be Shaped, Routed and Mitered
- Fasten Close to the Edge without Splits
- Can be Milled, Molded or Heat Formed for Custom Applications
|
| |
BEAUTY
- Compliments All Housing Exteriors
- Natural Looking Surface Provides Great Looks that Last
- Accepts Paint Easily for Custom Color
- Looks, Sounds and Feels Like White Painted Wood Trim
|
WARRANTY
Coverbord™ carries a full, 25 year non-prorated warranty. |
| |
TYPICAL TRIM SIZES
Coverbord™ is available in wood grain, matte or smooth finish. Coverbord™ is available in thicknesses of 3/8", 1/2", 5/8", 3/4", 7/8", and 1" (10, 13, 16, 19, 22, and 25 mm). Custom widths and lengths are available upon request.
Physical Properties |
Property
(ASTM Method) |
Conditions |
Units |
Value |
| Density (D-1505) |
|
lb/ft3 |
34.95 |
| Water Absorption (D-570) |
24 hrs. @ 73° |
|
0.5 |
Heat Deflection
Temp. (D-648) |
Load
264 psi |
°F |
138-145 |
| VICAT (D-1525) |
|
°F |
165-167 |
Coefficient of Linear
Thermal Expansion (D-696) |
|
in./in. °F |
3.7 x 10-15 |
Thermal Conductivity
(C-177) |
|
Btu-in./
hr. ft. - °F
|
0.49 |
| Surface Resistance (D-257)* |
|
Ohm |
5 x 1015 |
| Volume Resistance (D-257)* |
|
Ohm-cm |
5 x 1015 |
| |
|
|
Machine
Direction |
Transverse
Direction |
| Tensile Strength at Yield |
0.4 in./min. |
spi |
2,160-
2,300 |
1,100-
1,300 |
| Tensile Strength at Break |
0.4 in./min. |
spi |
2,050-
2,180 |
1,200-
1,300 |
| Elongation at Yield |
0.4 in./min. |
% |
2-3 |
10-11 |
| Elongation at Break (D-638)* |
0.4 in./min. |
% |
29-30 |
10-11 |
| Flexural Stress at Yield (D-790)* |
0.4 in./min. |
spi |
3,900-
4,050 |
1,900-
2,050 |
| Impact Strength Notched Charpy (D-256)* |
73 °F |
ft.lbf/
in. |
0.62-
0.66 |
0.62-
0.66 |
| Impact Strength Notched Izod (D-256)* |
73 °F |
ft.lbf/
in. |
051-
0.54 |
0.23-
0.24 |
*The method used may not be suitable for formed sheets.
|
| |
|